DuPont Performance Polymers Zytel® 7335F NC010 Nylon 6 (Unverified Data**)
Polymer,Thermoplastic,Nylon,Nylon 6
DuPont Performance Polymers
产品说明:
Zytel® 7335F NC010 is a nucleated, lubricated polyamide 6 resin for injection molding.
Information provided by DuPont Performance Polymers
DuPont Performance Polymers Zytel® 7335F NC010 Nylon 6 (Unverified Data**) 物性表（PA6 7335F最新价格）
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.13 g/cc | 0.0408 lb/in³ | DAM; ISO 1183 |
| Water Absorption | 3.0 % @Temperature 23.0 °C | 3.0 % @Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to |
| 9.0 % @Temperature 23.0 °C | 9.0 % @Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |
| 线性成型收缩率 | 0.0075 cm/cm @Thickness 1.60 mm | 0.0075 in/in @Thickness 0.0630 in | DAM |
| 0.010 cm/cm @Thickness 3.20 mm | 0.010 in/in @Thickness 0.126 in | DAM | |
| 线性成型收缩率,Flow | 0.0060 cm/cm @Thickness 2.00 mm | 0.0060 in/in @Thickness 0.0787 in | DAM; ISO 294-4 |
| 线性成型收缩率，横向 | 0.0080 cm/cm @Thickness 2.00 mm | 0.0080 in/in @Thickness 0.0787 in | DAM; ISO 294-4 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(屈服) | 55.0 MPa @Temperature 23.0 °C | 7980 psi @Temperature 73.4 °F | 50%RH; ISO 527 |
| 90.0 MPa @Temperature 23.0 °C | 13100 psi @Temperature 73.4 °F | DAM; ISO 527 | |
| 伸长率 (断裂) | 9.0 % @Temperature 23.0 °C | 9.0 % @Temperature 73.4 °F | DAM; nominal; ISO 527 |
| 15 % @Temperature 23.0 °C | 15 % @Temperature 73.4 °F | 50mm/min; DAM; ISO 527 | |
| >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | 50mm/min; 50%RH; ISO 527 | |
| >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | 50%RH; nominal; ISO 527 | |
| Elongation at Yield | 3.8 % @Temperature 23.0 °C | 3.8 % @Temperature 73.4 °F | DAM; ISO 527 |
| 24 % @Temperature 23.0 °C | 24 % @Temperature 73.4 °F | 50%RH; ISO 527 | |
| 拉伸模量 | 1.40 GPa @Temperature 23.0 °C | 203 ksi @Temperature 73.4 °F | 50%RH; ISO 527 |
| 3.60 GPa @Temperature 23.0 °C | 522 ksi @Temperature 73.4 °F | DAM; ISO 527 | |
| 简支梁无缺口冲击强度 | 6.00 J/cm² @Temperature -30.0 °C | 28.6 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eU |
| 7.00 J/cm² @Temperature 23.0 °C | 33.3 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eU | |
| 11.0 J/cm² @Temperature -30.0 °C | 52.3 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eU | |
| 12.0 J/cm² @Temperature 23.0 °C | 57.1 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |
| 简支梁缺口冲击强度 | 0.250 J/cm² @Temperature -30.0 °C | 1.19 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eA |
| 0.300 J/cm² @Temperature -30.0 °C | 1.43 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eA | |
| 0.450 J/cm² @Temperature 23.0 °C | 2.14 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | |
| 1.80 J/cm² @Temperature 23.0 °C | 8.57 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eA |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | 1.00e+11 ohm-cm @Temperature 23.0 °C | 1.00e+11 ohm-cm @Temperature 73.4 °F | 50%RH; ASTM D257 |
| 1.00e+11 ohm-cm @Temperature 23.0 °C | 1.00e+11 ohm-cm @Temperature 73.4 °F | 50%RH; IEC 60093 | |
| >= 1.00e+15 ohm-cm @Temperature 23.0 °C | >= 1.00e+15 ohm-cm @Temperature 73.4 °F | DAM; IEC 60093 | |
| 1.00e+17 ohm-cm @Temperature 23.0 °C | 1.00e+17 ohm-cm @Temperature 73.4 °F | DAM; ASTM D257 | |
| 1.00e+17 ohm-cm @Temperature 23.0 °C | 1.00e+17 ohm-cm @Temperature 73.4 °F | DAM; IEC 60093 | |
| Surface Resistance | 1.00e+11 ohm @Temperature 23.0 °C | 1.00e+11 ohm @Temperature 73.4 °F | 50%RH; ASTM D257 |
| 1.00e+11 ohm @Temperature 23.0 °C | 1.00e+11 ohm @Temperature 73.4 °F | 50%RH; IEC 60093 | |
| 1.00e+13 ohm @Temperature 23.0 °C | 1.00e+13 ohm @Temperature 73.4 °F | DAM; ASTM D257 | |
| 介电常数 | 3.3 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 3.3 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; ASTM D150 |
| 3.6 @Frequency 100 Hz, Temperature 23.0 °C | 3.6 @Frequency 100 Hz, Temperature 73.4 °F | DAM; ASTM D150 | |
| 3.6 @Frequency 1000 Hz, Temperature 23.0 °C | 3.6 @Frequency 1000 Hz, Temperature 73.4 °F | DAM; ASTM D150 | |
| 4.2 @Frequency 100 Hz, Temperature 23.0 °C | 4.2 @Frequency 100 Hz, Temperature 73.4 °F | DAM; IEC 60250 | |
| 介电强度 | 13.5 kV/mm @Thickness 3.20 mm, Temperature 23.0 °C | 343 kV/in @Thickness 0.126 in, Temperature 73.4 °F | 50%RH; Short Time; ASTM D149 |
| 16.3 kV/mm @Thickness 3.20 mm, Temperature 23.0 °C | 414 kV/in @Thickness 0.126 in, Temperature 73.4 °F | DAM; Short Time; ASTM D149 | |
| 耗散因数 | 0.010 @Frequency 1000 Hz, Temperature 23.0 °C | 0.010 @Frequency 1000 Hz, Temperature 73.4 °F | DAM; ASTM D150 |
| 0.010 @Frequency 100 Hz, Temperature 23.0 °C | 0.010 @Frequency 100 Hz, Temperature 73.4 °F | DAM; ASTM D150 | |
| 0.020 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.020 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; ASTM D150 | |
| 0.030 @Frequency 100 Hz, Temperature 23.0 °C | 0.030 @Frequency 100 Hz, Temperature 73.4 °F | DAM; IEC 60250 | |
| 0.11 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.11 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | 50%RH; ASTM D150 | |
| 0.23 @Frequency 1000 Hz, Temperature 23.0 °C | 0.23 @Frequency 1000 Hz, Temperature 73.4 °F | 50%RH; ASTM D150 | |
| 0.37 @Frequency 100 Hz, Temperature 23.0 °C | 0.37 @Frequency 100 Hz, Temperature 73.4 °F | 50%RH; ASTM D150 | |
| 相比耐漏电起痕指数(CTI) | 600 V @Temperature 23.0 °C | 600 V @Temperature 73.4 °F | DAM; IEC 60112 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 |
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |
| 线性热膨胀系数,横向流动 | 92.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 51.1 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 |
| 92.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 51.1 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |
| 熔融温度 | 221 °C | 430 °F | 10°C/min; DAM; ISO 11357-1/-3 |
| 载荷下热变形温度(0.46 MPa) | 175 °C | 347 °F | DAM; ISO 75-1/-2 |
| 载荷下热变形温度(1.8 MPa) | 65.0 °C | 149 °F | DAM; ISO 75-1/-2 |
| 可燃性(UL94) | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; UL94 |
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | 260 - 280 °C | 500 - 536 °F | DAM |
| 270 °C | 518 °F | DAM; Optimum | |
| 模具温度 | 70.0 °C | 158 °F | DAM; optimum |
| 50.0 - 90.0 °C | 122 - 194 °F | DAM | |
| 干燥温度 | 80.0 °C | 176 °F | DAM |
| 干燥时间 | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM |
| 水分含量 | <= 0.20 % | <= 0.20 % | DAM |
| 材料描述 | 测试方法 | |
|---|---|---|
| 添加剂 | Lubricant | DAM |
| 外观 | Natural Color | DAM |
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM |
| 特性 | Chemical Resistance, Good | DAM |
| Fatigue Resistant | DAM | |
| Fuel Resistant | DAM | |
| General Purpose | DAM | |
| Grease Resistant | DAM | |
| Mold Release, Good | DAM | |
| Nucleated | DAM | |
| Oil Resistant | DAM | |
| 形式 | Pellets | DAM |
| Generic | Nylon 6 | DAM |
| Material Status | Current | DAM |
| 部件标识代码 | >PA6< | ISO 11469; DAM |
| Polymer Family | Polyamide | DAM |
| Polymer Type | PA6 | DAM |
| 加工方法 | Injection Molding | DAM |
| 产品分类 | Unreinforced Resins | DAM |
| 树脂识别 | PA6 | ISO 1043; DAM |
| 符合RoHS指令 | Contact Manufacturer | DAM |
| Ultrasonic Weldable | Yes | DAM |
| 用途 | Appliance Components | DAM |
| Automotive Applications | DAM |